PA6(尼龙6)BG30XF30/德国朗盛/物性表参数

日期：2020-04-25 02:35:00 编辑：科思德塑胶来源：科思德塑胶浏览：329

德国朗盛LANXESS Durethan PA6 BG30XF30是一种加30%玻璃/玻璃球，注塑，阻燃剂，低倾向于翘曲，改善表面光洁度尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
生产商：LANXESS(德国朗盛)、品名：Durethan
PA6(尼龙6)BG30XF30/德国朗盛/物性表参数

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.4
	Molding shrinkage, transverse	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.7
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	7500	4200
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	105	65
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.7	4.4
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	40	45
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	30	35
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	<10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	40	45
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	30	35
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	7300	4200
	Flexural strength	2 mm/min	MPa	ISO 178-A	175	120
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	2.8	4.2
	Puncture maximum force	23 °C	N	ISO 6603-2	650
	Puncture maximum force	-30 °C	N	ISO 6603-2	550
	Puncture energy	23 °C	J	ISO 6603-2	2.4
	Puncture energy	-30 °C	J	ISO 6603-2	1.8
	Ball indentation hardness		N/mm²	ISO 2039-1	210
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	185
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	210
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.3
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94	0.75 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V	1.5 mm	Class	UL 94	5VA
	Oxygen index	Method A	%	ISO 4589-2	32
	Resistance to heat (ball pressure test)		°C	IEC 60695-10-2	200
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	825
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	800
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	825
Electrical properties (23 °C/50 % r. h.)
	Electric strength	1 mm	kV/mm	IEC 60243-1	33
	Comparative tracking index CTI	Solution A	PLC	UL 746A	1
Other properties (23 °C)
C	Density		kg/m³	ISO 1183	1630
	Bulk density		kg/m³	ISO 60	880
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-100

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：PA6(尼龙6)BG30X/德国朗盛/物性表参数下一页：PA6(尼龙6)BG30XH2.0/德国朗盛/物性表参数

返回世界杯shijiebei（中国）返回物性参数列表

PA6(尼龙6)BG30XF30/德国朗盛/物性表参数

热门文章

推荐文章