PA6(尼龙6)BKV50H3.0/德国朗盛/物性表参数

日期：2020-04-14 10:03:11 编辑：科思德塑胶来源：科思德塑胶浏览：225

德国朗盛LANXESS Durethan PA6 BKV50H3.0是一种加入50%玻璃纤维，注塑，改善流动性，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BKV50H3.0

以下是PA6(尼龙6)BKV50H3.0/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 280 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.16
	Molding shrinkage, transverse	150x105x3; 280 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.85
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.02
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.05
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	16800	10200
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	225	140
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.0	5.0
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	100	110
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	90	90
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	20	25
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	15	15
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	95	100
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	95	95
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	20	25
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	15	15
	Flexural modulus	2 mm/min	MPa	ISO 178-A	15500	9900
	Flexural strength	2 mm/min	MPa	ISO 178-A	360	230
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.0	5.0
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	205
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	215
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.7
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Burning behavior UL 94	0.75 mm	Class	UL 94	HB
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Burning behavior US-FMVSS302	>=1.0 mm		ISO 3795	passed
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	> 200
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	5.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.5
	Density		kg/m³	ISO 1183	1570
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.