PA66(尼龙66)AKV30HRH2.0/德国朗盛/物性表参数

日期：2020-04-25 03:03:48 编辑：科思德塑胶来源：科思德塑胶浏览：347

德国朗盛Durethan PA66 AKV30HRH2.0是一种加30%玻璃纤维p66, 注塑成型，热老化稳定，表面光洁度提高尼龙树脂,根据特定的材料及所需等级，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA66 AKV30HRH2.0

生产商：LANXESS(德国朗盛)、品名：Durethan
PA66(尼龙66)AKV30HRH2.0/德国朗盛/物性表参数

C	These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
C	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.44
C	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.94
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.06
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.12
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	9700	6100
C	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	180	120
C	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.5	8.0
C	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	75	85
C	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	65	75
C	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	10	20
C	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Charpy notched impact strength	-40 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	70
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	60
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Izod notched impact strength	-40 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	9300	5700
	Flexural strength	2 mm/min	MPa	ISO 178-A	280	180
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.0	6.5
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	265	150
C	Puncture maximum force	23 °C	N	ISO 6603-2	896	1073
C	Puncture maximum force	-30 °C	N	ISO 6603-2	776
C	Puncture energy	23 °C	J	ISO 6603-2	3.1	4.7
C	Puncture energy	-30 °C	J	ISO 6603-2	1.9
	Ball indentation hardness		N/mm²	ISO 2039-1	205	105
Thermal properties
C	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	262
C	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	245
C	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	250
C	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	125
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	254
C	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.3
C	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
C	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
C	Burning behavior UL 94	0.75 mm	Class	UL 94	HB
C	Oxygen index	Method A	%	ISO 4589-2	26
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Burning behavior US-FMVSS302	>=1.0 mm		ISO 3795	passed
C	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	> 230
Electrical properties (23 °C/50 % r. h.)
C	Relative permittivity	100 Hz	-	IEC 60250	4.0	12
C	Relative permittivity	1 MHz	-	IEC 60250	3.6	4.5
C	Dissipation factor	100 Hz	10-4	IEC 60250	80	3000
C	Dissipation factor	1 MHz	10-4	IEC 60250	160	900
C	Volume resistivity		Ohm·m	IEC 60093	1E13	1E09
C	Surface resistivity		Ohm	IEC 60093	1E15	1E13
C	Electric strength	1 mm	kV/mm	IEC 60243-1	35	30
C	Comparative tracking index CTI	Solution A	Rating	IEC 60112	450
Other properties (23 °C)
C	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	5.5
C	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	2.0
C	Density		kg/m³	ISO 1183	1360
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
C	Injection molding-Melt temperature		°C	ISO 294	290
C	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

德国朗盛Durethan PA66 AKV30HRH2.0具有高抗震及抗裂性能，具体指标与材料的等级与含水量有关。弹性体改性的材料即使在低含水量及低温下也具有良好的韧性,硬度高，尤其对于玻纤增強级别产品；拉伸模量：1,300 到 15,700 MPa (取决于含水量),良好的机械性能及阻尼吸声效应、低摩擦力、急速运行能力好，气体阻隔性能好（薄膜级）,

密度	1.01~1.23	模具温度	80.0 到 100°C
加工（熔体）温度	260 到 270°C	注射压力	230 到 250°C
预热	温度/°C	130°C	工艺参数	注射时间	20~90
时间/h	4.0hr	高压时间	0~5
料桶温度/°C	后段	193 到 238°C	冷却时间	20~90
中段	210 到 249°C	总周期	220 到 260°C
前段	221 到 254°C	螺杆转数	30 到 60rpm
喷嘴温度	232 到 274°C	使用注射机类型	螺杆式

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.