德国朗盛LANXESS Durethan PA6 B31SKH3.0是一种无强化，注塑成型，热老化稳定尼龙6树脂,根据特定的材料及所需等级，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
生产商：LANXESS(德国朗盛)、品名：Durethan
PA6(尼龙6)B31SKH3.0/德国朗盛/物性表参数

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 270 °C / WZ 80 °C; 600 bar	%	ISO 294-4	0.9
	Molding shrinkage, transverse	60x60x2; 270 °C / WZ 80 °C; 600 bar	%	ISO 294-4	1.1
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.15
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.15
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	3700	1100
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	90	55
	Yield strain	50 mm/min	%	ISO 527-1,-2	4	20
	Nominal strain at break	50 mm/min	%	ISO 527-1,-2	10	>50
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	N	N
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	N	N
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	25
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	115	N
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	115	N
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	3000	900
	Flexural strength	2 mm/min	MPa	ISO 178-A	120	40
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	6	8
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	100	30
	Puncture maximum force	23 °C	N	ISO 6603-2	4600
	Puncture maximum force	-30 °C	N	ISO 6603-2	6800
	Puncture energy	23 °C	J	ISO 6603-2	46
	Puncture energy	-30 °C	J	ISO 6603-2	70
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	60
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	170
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.7
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior US-FMVSS302			ISO 3795	passed
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	3
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	10
	Density		kg/m³	ISO 1183	1140
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	270
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	260-280
	Mold temperature		°C	-	80-100

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：PA6(尼龙6)B31SK/德国朗盛/物性表参数下一页：PA6(尼龙6)B31SKH3.0LT/德国朗盛/物性表参数

返回世界杯shijiebei（中国）返回物性参数列表

PA6(尼龙6)B31SKH3.0/德国朗盛/物性表参数

热门文章

推荐文章