PA6(尼龙6)BKV130GIT/德国朗盛/物性表参数

日期：2020-04-25 02:30:15 编辑：科思德塑胶来源：科思德塑胶浏览：294

德国朗盛LANXESS Durethan PA6 BKV130GIT是一种加30%玻璃纤维，注塑成型，提高冲击强度，GIT/WIT6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。

生产商：LANXESS(德国朗盛)、品名：Durethan
PA6(尼龙6)BKV130GIT/德国朗盛/物性表参数

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 280 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.13
	Molding shrinkage, transverse	150x105x3; 280 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.64
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.04
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.14
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	8800	5000
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	160	95
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.5	8.9
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	85	85
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	65	60
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	15	20
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	10	10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	75	75
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	60	50
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	15	15
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	10	10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	8200	4500
	Flexural strength	2 mm/min	MPa	ISO 178-A	250	140
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.0	7.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	220	110
	Puncture maximum force	23 °C	N	ISO 6603-2	919
	Puncture maximum force	-30 °C	N	ISO 6603-2	772
	Puncture energy	23 °C	J	ISO 6603-2	9	13
	Puncture energy	-30 °C	J	ISO 6603-2	6
	Ball indentation hardness		N/mm²	ISO 2039-1	180
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	213
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	190
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	210
	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	80
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	24
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Burning behavior US-FMVSS302			ISO 3795	34
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	200
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.5	12
	Relative permittivity	1 MHz	-	IEC 60250	4.0	4.5
	Dissipation factor	100 Hz	10-4	IEC 60250	70	1600
	Dissipation factor	1 MHz	10-4	IEC 60250	200	900
	Volume resistivity		Ohm·m	IEC 60093	1E13	1E10
	Surface resistivity		Ohm	IEC 60093	1E15	1E14
	Electric strength	1 mm	kV/mm	IEC 60243-1	32	32
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
	Comparative tracking index CTI M	Solution B	Rating	IEC 60112	400 (325) M 1- 1.5
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	6.5
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.9
	Density		kg/m³	ISO 1183	1360
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	260-290
	Mold temperature		°C	-	80-100

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：PA6(尼龙6)BKV130CS/德国朗盛/物性表参数下一页：PA6(尼龙6)BKV130H2.0/德国朗盛/物性表参数

返回世界杯shijiebei（中国）返回物性参数列表

PA6(尼龙6)BKV130GIT/德国朗盛/物性表参数

热门文章

推荐文章