PA6(尼龙6)BKV20FN01/德国朗盛/物性表参数

日期：2020-04-25 02:27:19 编辑：科思德塑胶来源：科思德塑胶浏览：381

德国朗盛LANXESS Durethan PA6 BKV20FN01是一种加18%玻璃纤维，注塑，提高流动性，表面光洁度，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。

生产商：LANXESS(德国朗盛)、品名：Durethan
PA6(尼龙6)BKV20FN01/德国朗盛/物性表参数

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Melt volume-flow rate	260 °C; 5 kg	cm³/(10 min)	ISO 1133-1	37
	Molding shrinkage, parallel	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.3
	Molding shrinkage, transverse	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.6
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.2
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	7960	4500
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	105	60
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.0	4.9
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	50	60
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	12
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	40	45
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	12
	Flexural modulus	2 mm/min	MPa	ISO 178-A	7200	4200
	Flexural strength	2 mm/min	MPa	ISO 178-A	170	110
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.2	6.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A		95
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	218
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	205
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.3
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94	0.75 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V	3.0 mm	Class	UL 94	5VA
	Oxygen index	Method A	%	ISO 4589-2	34
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	750
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	750
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	750
Electrical properties (23 °C/50 % r. h.)
	Volume resistivity		Ohm·m	IEC 60093	5.3E15
	Surface resistivity		Ohm	IEC 60093	8.6E15
	Comparative tracking index CTI	Solution A	PLC	UL 746A	0
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	5.3
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.6
	Density		kg/m³	ISO 1183	1340
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	260
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.07
	Melt temperature (Tmin - Tmax)		°C	-	250-270
	Mold temperature		°C	-	80-100

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.

上一页：PA6(尼龙6)BKV15W/德国朗盛/物性表参数下一页：PA6(尼龙6)BKV20FN20/德国朗盛/物性表参数

返回世界杯shijiebei（中国）返回物性参数列表

PA6(尼龙6)BKV20FN01/德国朗盛/物性表参数

热门文章

推荐文章