PA6(尼龙6)BKV30GW1/德国朗盛/物性表参数

日期：2020-04-14 09:48:59 编辑：科思德塑胶来源：科思德塑胶浏览：279

德国朗盛LANXESS Durethan PA6 BKV30GW1是一种加入30%玻璃纤维，注塑，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BKV30GW1

以下是PA6(尼龙6)BKV30GW1/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.2
	Molding shrinkage, transverse	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.6
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.2
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	9900	6600
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	180	106
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.7	6.1
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	60	65
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	50	40
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	50	60
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	45	40
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	10	10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	8700	6300
	Flexural strength	2 mm/min	MPa	ISO 178-A	270	177
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.7	5.7
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	260	156
	Puncture maximum force	23 °C	N	ISO 6603-2	840
	Puncture maximum force	-30 °C	N	ISO 6603-2	740
	Puncture energy	23 °C	J	ISO 6603-2	3.0
	Puncture energy	-30 °C	J	ISO 6603-2	2.0
	Ball indentation hardness		N/mm²	ISO 2039-1	209
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	219
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	215
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	211
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.3
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.8
	Burning behavior US-FMVSS302			ISO 3795	passed
Electrical properties (23 °C/50 % r. h.)
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	500
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	6.4
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	2.0
	Density		kg/m³	ISO 1183	1365
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.