德国朗盛LANXESS Durethan PA6 BKV40H2.0是一种加入40%玻璃纤维，注塑，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BKV40H2.0

以下是PA6(尼龙6)BKV40H2.0/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 280 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.16
	Molding shrinkage, transverse	150x105x3; 280 °C / MT 80 °C; 400 bar	%	acc. ISO 2577	0.85
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.03
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.07
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	11900	7800
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	195	130
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.0	6.0
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	95	90
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	85	70
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	15	20
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	18	24
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	13	11
	Flexural modulus	2 mm/min	MPa	ISO 178-A	11200	7300
	Flexural strength	2 mm/min	MPa	ISO 178-A	310	200
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	4.0	5.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	305	170
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	215
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 200
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.0	10
	Relative permittivity	1 MHz	-	IEC 60250	4.0	5.0
	Dissipation factor	100 Hz	10-4	IEC 60250	50	2500
	Dissipation factor	1 MHz	10-4	IEC 60250	150	1200
	Volume resistivity		Ohm·m	IEC 60093	1E13	1E09
	Surface resistivity		Ohm	IEC 60093	1E14	1E10
	Electric strength	1 mm	kV/mm	IEC 60243-1	40	35
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	400
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	6.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.8
	Density		kg/m³	ISO 1183	1460
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.