PA6(尼龙6)BTC75H3.0EF/德国朗盛/物性表参数

日期：2020-04-14 10:15:55 编辑：科思德塑胶来源：科思德塑胶浏览：266

德国朗盛LANXESS Durethan PA6 BTC75H3.0EF是一种加入75%矿物填充，注塑，提高导热，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同,这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BTC75H3.0EF

以下是PA6(尼龙6)BTC75H3.0EF/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.6
	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.7
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	14700	6100
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	90	50
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	1.8	2.2
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	28	26
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	18	11
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	<10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	23	18
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	20	12
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	16000	6500
	Flexural strength	2 mm/min	MPa	ISO 178-A	170	80
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	2	2.1
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	221
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	160
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	200
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	210
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.4
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.4
	Thermal conductivity, with flow		W/(m·K)	ISO 22007-4	1.7
	Thermal conductivity, through-plane		W/(m·K)	ISO 22007-4	1.4
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	775
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	750
	Burning behavior US-FMVSS302			ISO 3795	passed
Electrical properties (23 °C/50 % r. h.)
	Volume resistivity		Ohm·m	IEC 60093	1.00E+15
	Surface resistivity		Ohm	IEC 60093	1.00E+13
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	2.5
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	0.8
	Density		kg/m³	ISO 1183	2290
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	290
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.