VALOX(沙伯基础)735/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 735 PBT是一种加40%玻璃/矿物，优异的热工性能/低收缩,电动加热设备，适配器环，烤箱烤架等,提供黑色/自然色。
 |
沙伯基础创新塑料的VALOX 735 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)735/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8300 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 64 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 130 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 130 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 2 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 144 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 124 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 40 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 30 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 560 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 520 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 55 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| Thermal Conductivity | 0.36 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 2.28E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.53E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.18E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.4E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 180 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.62 | - | ASTM D 792 | |
| Filler Content | 40 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.8 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 20 | g/10 min | ASTM D 1238 | |
| Density | 1.62 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.96 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 1 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 3 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 15 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 160 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 45 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 45 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.008 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.017 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.5 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.81 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 4 - 6 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260 - 285 | °C | ||
| Nozzle Temperature | 265 - 275 | °C | ||
| Front - Zone 3 Temperature | 260 - 280 | °C | ||
| Middle - Zone 2 Temperature | 255 - 280 | °C | ||
| Rear - Zone 1 Temperature | 240 - 260 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 60 - 110 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：12067 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：10656 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：10407 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：8719 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：7728 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：7696 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：7200 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：6679 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：6339 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：6305 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：6290 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：6189 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：6027 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5922 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：5859
推荐文章
-
PC(聚碳酸酯)3208/科思创(Makrolon)物性表参数
科思创(原德国拜耳)Makrolon(模克隆) PC 3208 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 5.0cm cm /10 min，高粘度，适用于121℃的ETO和蒸汽灭菌;符合多项ISO 10993-1测试要求的生物相容性，
-
PA66(尼龙66)2104T/神马(Shenma)物性表参数
神马(Shenma)PA662104T是一种增韧型尼龙66，耐低温、高抗冲击，用于铁路槽型板、汽车门锁、管件。以下是PA66(尼龙66)2104T/神马(Shenma)物性表参数产品特性高冲击耐低温冲击增韧/冲击改性技术参数冲击性能值/单位测试标准测试条件简支梁无缺口(Charpy Unnotched)-NB kJ/m²ISO 179温馨提示：本物性表参数提供者
-
PC(聚碳酸酯)WB1239/科思创(Makrolon)物性表参数
科思创(Covestro)模克隆(Makrolon) PC WB1239 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 2.0cm cm /10 min，吹塑;高粘度;支;食品接触级别，应用于水瓶产品。 以下是PC(聚碳酸酯)WB1239/科思创
-
ULTEM(沙伯基础)AUR200G6|PEI(聚醚酰亚胺)物性表参数
SABIC(沙伯基础)ULTEM AUR200G6 PEI 树脂的该数据表中所列的数据是较低的规格限制，除了MFR、CTE、HDT 1.8 MPa、密度、拉伸应变、吸水、热导率和收缩，这些都是典型的数据。这种材料在337度的
-
POM(聚甲醛树脂)CH-20/日本宝理/物性表参数
日本宝理夺钢DURACON POM CH-20 是一种导电级,CF15%增强, 耐磨耗性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu
-
EAA(乙烯-丙烯酸共聚物)5050/埃克森美孚(ExxonMobil)物性表参数
埃克森美孚(ExxonMobil)Escor EAA 5050主要用于挤出涂覆、共挤涂覆和挤出复合乙烯-丙烯酸共聚物，熔体流动速率(230°C/2.16kg)是8.4克/10分钟，丙烯酸含量9.0(wt%)，EAA 5050可良好地粘合于极性基材、铝箔、金属膜、纸张、钢铁和玻璃表面， 提供与基材表面的粘合性和与共挤的低密度聚乙烯和乙烯醋酸乙烯酯的层间结合力
-
TPU(热塑性聚氨酯)11H94/路博润(Lubrizol)物性表参数
路博润(Lubrizol)Pearlthane TPU 11H94是一种以聚己内酯共聚酯为基础的热塑性聚氨酯，肖氏硬度95A，特点是刚性等级高，具有优异的耐化学性和耐油性，本系列旨在满足对广泛技术应用日益严格的需求，例如高柔韧性薄膜、耐磨软管、柔软注塑部件或特殊化合物。，主要用于注塑成型应用。以下是TPU(热塑性聚氨酯)11H94/路博润(Lub
-
GPPS(通用级聚苯乙烯)656D/盛禧奥/物性表参数
盛禧奥STYRON GPPS 656D是一种通用聚苯乙烯树脂拥有高流动性及高透明度的特性，适用于对加工性能及产品强度有严格要求的应用。密度是1.04(g/cm³)，熔流率（熔体流动速率） (200°C/5.0 kg)8.5g/10 min。以下是GPPS(通用级聚苯乙烯)656D/盛禧奥/物性表参数基本信息黄卡编号E73656-249599特性良好的流动性良好的强度清晰度，
-
PA66(尼龙66)22G5/长春化工(漳州)/物性表参数
长春化工(漳州)NYLON(尼龙) PA66 22G5 -104(黑色)/201(本色)是一种加25%玻璃纤维增强，无卤阻燃尼龙66树脂，优越的机械与抗压强度，高抗燃料、油料、溶剂特性，25㎏/aluminum foil bag(铝箔纸袋包
-
PPS(聚苯硫醚)R-4|SOLVAY(索尔维)物性表参数
SOLVAY(索尔维)Ryton PPS R-4 是一款添加40%玻璃纤维，自然色聚苯硫醚原料，特性是摩擦低、耐磨性好，材料优势是可精密成型、阻燃、良好的电气性能、热固性树脂替代材料、耐热冲击，应