LEXAN(沙伯基础)505R/PC(聚碳酸酯)物性表参数
沙伯基础SABIC塑料LEXAN 505R聚碳酸酯（PC）是一种可注射成型的非氯化和非溴化阻燃级，填充10％玻璃纤维, 它具有UL94 V0@1.5mm的额定值，并提供各种不透明颜色选项, 这是LEXAN 500,500R，500RS，500ECR的替代品。
 |
沙伯基础SABIC塑料LEXAN 505R PC物性表参数PDF文档下载 |
以下是LEXAN(沙伯基础)505R/PC(聚碳酸酯)物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 63 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 48 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 12 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 3930 | MPa | ASTM D 638 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 108 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3530 | MPa | ASTM D 790 | |
| Hardness, Rockwell M | 85 | - | ASTM D 785 | |
| Hardness, Rockwell R | 124 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 11 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 60 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 3300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 95 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3400 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 115 | MPa | ISO 2039-1 | |
| IMPACT | ||||
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 107 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 61 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | 130 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m² | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 15 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Specific Heat | 1.21 | J/g-°C | ASTM C 351 | |
| Thermal Conductivity | 0.2 | W/m-°C | ASTM C177 | |
| Vicat Softening Temp, Rate B/50 | 149 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 143 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 138 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.68E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.46E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.21 | W/m-°C | ISO 8302 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 141 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 143 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 144 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Ae | |
| HDT/Ae, 1.8 MPa Annealed 120°C, 2hrs | 136 | °C | ISO 75/Ae | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Af | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Bf | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.26 | - | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.13 | % | ASTM D 570 | |
| Water Absorption, 24 hours | 0.12 | % | ASTM D 570 | |
| Water Absorption, equilibrium, 23C | 0.31 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow | 0.2-0.6 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
| Melt Flow Rate, 300°C/1.2 kgf | 7 | g/10 min | ASTM D 1238 | |
| Density | 1.25 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.31 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.13 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 7 | cm³/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 33 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.8 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 2.9 | - | IEC 60250 | |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94-5VA Flame Class Rating | 3 | mm | UL 94 | |
| UL Compliant, 94-5VB Rating | 2 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 | |
| Oxygen Index (LOI) | 37 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 290-320 | °C | ||
| Nozzle Temperature | 280-310 | °C | ||
| Front - Zone 3 Temperature | 290-320 | °C | ||
| Middle - Zone 2 Temperature | 280-310 | °C | ||
| Rear - Zone 1 Temperature | 270-300 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 80-120 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：12045 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：10636 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：10392 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：8703 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：7724 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：7687 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：7197 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：6675 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：6329 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：6302 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：6278 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：6185 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：6021 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5913 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：5842
推荐文章
-
PA6(尼龙6)1021GF6|索尔维(SOLVAY)物性表参数
索尔维(SOLVAY)(原罗地亚)TECHNYL PA6 1021GF6是一种加30%的玻璃纤维增强尼龙6(PA6)树脂，热稳定性能良好，用于注射成型，这种产品有鲜艳的颜色可供选择。以下是PA6(尼龙6)1021GF6|索尔维(SOLVAY)物性表参数基本信息填料/增强材料玻璃纤维增强材料,30% 填料按重量机构评级UU 453/2010/ECRoHS 合规性RoHS 合规外观可用颜色
-
PP(聚丙烯)B330F/韩国SK/物性表参数
韩国SK Global Chemical Yuplene PP B330F是一种为注射成形的而研制的抗冲击聚丙烯，它具有很好的耐冲性和数指稳定性，因此已获得了 UL认证，可广泛使用在一般生活用品、椅子、容器及汽车零件中，熔体流动速率(230°C/2.16kg)3.5克/10分钟，YUPLENE B330F满足一切食品接触的FDA规21CER177.1520。以下是PP(聚丙烯)B330F/
-
PC(聚碳酸酯)EHR3200|三菱工程塑料|物性表参数
三菱工程塑料Iupilon/NOVAREX/XANTAR PC EHR3200是光反射,高遮光品级; 无溴无磷阻燃,体积熔融指数26厘米3/10分钟; 易脱模; 注塑成型,三菱工程研究开发成功的聚碳酸酯，在市场上已有好多年历史, 被广泛地用于各种工业生产，如运动器械、医疗器械、汽车部件、光学仪器、机械、办公自动化设备和电子设备，获得了客户的广
-
SPS(间规聚苯乙烯)S131|出光兴产|物性表参数
出光兴产的XAREC SPS S131 是加30%玻璃纤维增强间规聚苯乙烯树脂，密度是1.25g/cm，拉伸模量是9700MPa，简支梁缺口冲击强度(23C)12kJ/m，UL阻燃等级 ( 0.800 mm) HB UL94，因分子规则排列，汽车,电子用
-
PA66(尼龙66)70G33L/塞拉尼斯/物性表参数
塞拉尼斯PA66 70G33L是一种聚酰胺66，加33%玻璃纤维增强，性能是增韧，颜色是NC010，BK031。原材料生产商：塞拉尼斯以下是PA66(尼龙66)70G33L/塞拉尼斯/物性表参数基本信息黄卡编号E41938-234410填料/增强材料玻璃纤维增强材料,33% 填料按重量添加剂润滑剂、脱模特性润滑形式粒子加工方法注射成型部件标识代码 (ISO 11469
-
PBT/PET(PBT+PET合金)865|沙伯基础|物性表参数
沙伯基础(SABIC)VALOX PBT/PET 865是聚对苯二甲酸丁二酯/聚对苯二甲酸乙二酯(PBT/PET)树脂是一种30种玻璃纤维增强、美观、低开度、注塑级，这种溴化阻燃剂PBT/PET具有UL V0等级，颜色选择有限。VALOX 865树脂是一种通用树脂，是广泛应用于蒸汽熨斗、电器和照明设备的选择。VALOX 865 PBT/PET物性表参数PDF文档下载生产商：S
-
PC/ABS（PC合金）GP5206F|LUPOY(LG化学)物性表参数
LG工程塑料LUPOY PC/ABS GP5206F详细介绍 PC/ABS GP5206F是玻璃纤维增强材料，广泛使用的塑料更硬、更轻，是用作工业材料高功能性塑料工程塑料中的一种。聚碳酸脂具有耐冲击性、耐热性。
-
TPE/G7736-1/TPE物性表参数
美国普立万（吉力士）GLS系列Dynaflex TPE G7736-1 是一种容易加工的通用型 TPE，容易加工并能产生良好的表面光洁度, 美学效果佳 、抗臭氧和抗紫外线性能佳、 流动性强，适用于薄壁部件
-
塞拉尼斯TPV 271-73|Santoprene 271-73物性表参数
Celanese(塞拉尼斯)SANTOPRENE(山都坪)TPV 271-73是一种热塑性硫化弹性体，TPV 271-73也是一种坚硬的、可着色的特种热塑性硫化胶(TPV)，它符合FDA关于重复使用的橡胶制品的规定，以及那些与非脂肪、非油性食品接触的橡胶制品，如封闭和密封垫片，该等级的Santoprene TPV是剪切依赖的，可以在传统的热塑性塑料设备上进行注
-
TOYOLAC(东丽)100G-23R|ABS塑料树脂|物性表参数
东丽TOYOLAC ABS 100G-23R 是一种加23%玻璃纤维，简支梁冲击强度是7/kJ/m 2 ，低翘曲级别的ABS树脂，广泛用在工业和家庭用品中，这是因为其具有一系列独特的性质（兼具强度、轻便性和