PC(聚碳酸酯)EXL1162T/沙伯基础(SABIC)物性表参数

日期：2020-06-12 05:06:19 编辑：科思德塑胶来源：科思德塑胶浏览：353

SABIC(沙伯基础创新塑料)LEXAN PC EXL1162T是聚碳酸酯(PC)硅氧烷共聚物树脂，也是一种透明注塑(IM)级，具有额外的释放性能，与标准PC树脂相比，该树脂具有良好的低温(-20 C)延展性，并具有高流动特性和优异的加工性能，IM循环时间更短。LEXAN EXL1162T树脂是一种通用产品，有透明和不透明的颜色。

PC(聚碳酸酯)EXL1162T/沙伯基础(SABIC)物性表参数PDF文档下载

以下是PC(聚碳酸酯)EXL1162T/沙伯基础(SABIC)物性表参数

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	58	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	57	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	5.7	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	117.9	%	ASTM D 638
Tensile Modulus, 50 mm/min	2260	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	94	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2240	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	57	MPa	ISO 527
Tensile Stress, break, 50 mm/min	56	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.4	%	ISO 527
Tensile Strain, break, 50 mm/min	119.4	%	ISO 527
Tensile Modulus, 1 mm/min	2340	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	89	MPa	ISO 178
Flexural Modulus, 2 mm/min	2140	MPa	ISO 178
Hardness, Rockwell L	89	-	ISO 2039-2
IMPACT
Izod Impact, notched, 23°C	736	J/m	ASTM D 256
Izod Impact, notched, -30°C	618	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	74	J	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80103 +23°C	55	kJ/m²	ISO 180/1A
Izod Impact, notched 80103 -30°C	40	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	65	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	45	kJ/m²	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate A/50	138	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	121	°C	ASTM D 648
CTE, -40°C to 95°C, flow	7.48E-05	1/°C	ASTM E 831
CTE, -40°C to 95°C, xflow	7.64E-05	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	7.48E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.64E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	pass	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	138	°C	ISO 306
Vicat Softening Temp, Rate B/120	139	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	116	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.19	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4-0.8	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.4-0.8	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf	20	g/10 min	ASTM D 1238
Density	1.19	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.12	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.09	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	19	cm³/10 min	ISO 1133
OPTICAL
Light Transmission, 2.54 mm	82	%	ASTM D 1003
Haze, 2.54 mm	3	%	ASTM D 1003
ELECTRICAL
Volume Resistivity	>1.E+15	Ohm-cm	ASTM D 257
Surface Resistivity	>1.E+15	Ohm	ASTM D 257
Injection Molding
Drying Temperature	120	°C
Drying Time	3-4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295-315	°C
Nozzle Temperature	290-310	°C
Front - Zone 3 Temperature	295-315	°C
Middle - Zone 2 Temperature	280-305	°C
Rear - Zone 1 Temperature	270-295	°C
Mold Temperature	70-95	°C
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	40-60	%
Vent Depth	0.025-0.076	mm

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
为及时发现和纠正网站存在的信息内容等方面问题，在使用网站时及时反馈网站问题，从而帮助推进网站信息内容建设工作，提高网站信息互动交流。

上一页：PC(聚碳酸酯)EXL1132T/沙伯基础(SABIC)物性表参数下一页：PC(聚碳酸酯)EXL1182T/沙伯基础(SABIC)物性表参数

返回世界杯shijiebei（中国）返回物性参数列表

PC(聚碳酸酯)EXL1162T/沙伯基础(SABIC)物性表参数

热门文章

推荐文章